IOTA HCR 160 U is a silicone master-batch, vulcanizing under heat after addition of a vulcanizing agent (chosen according to the transformation procedure).
HEAT CURED SILICONE RUBBER IOTA HCR 160 U
Description:IOTA HCR
160 U is a
silicone master-batch, vulcanizing under heat after addition of a vulcanizing
agent (chosen according to the transformation procedure).
Applications:
General purpose extrusion material: profiles, gasket and tubing.
Compression and injection moulding to manufacture high transparent or bright colored parts featuring good mechanical properties.
Special properties:
No milling or quick milling after long storage
Easy processing in milling, extrusion and moulding
No post-cure or slight post-cure
High transparency
Good heat stability, up to 200℃
High level of filler acceptance
Bright colors easily obtained with Bluestar Silicones SC color bases
Good mechanical and electrical properties
Blendable with other master-batches and additives.
Characteristics:
Type(in accordance with GB/T 5576/1997) ………………………………………… VMQ
Density at 25℃, g/cm3, approx………………………………………………………… 1.14
Natural color…………………………………………………………………… Transparent
Properties
after working:
(1) After addition of 1.25% 2,4-dichloro-benzoyl peroxide (at 50%), and vulcanization for 8min at 115℃
(2) After addition of 1.0% 2,5-dimethyl-2,5-di(tert-butylperoxy)hexane at 45%, and vulcanization for 10 minutes at 170℃
1. Mechanical properties
1.1 Properties without post-cure (1) (2)
Shore A hardness, approx………………………………. 59 56
Tensile strength, MPa, approx……………………………… 9.7 11.2
Elongation at break, %, approx…………………………… 400 520
Modulus at 100% elongatioin, MPa, approx ……………… 2.0 1.5
Tear strength, kN/m, approx………………………………… 21 24
Compression set (22h/177°C/25%), %, approx. ………… 44 35
Rebound resilience, %, approx………………………………… 54 46
1.2 Properties after post-cure for 4 hours at 200℃
Shore A hardness, approx……………………………………. 62 61
Tensile strength, MPa, approx………………………………… 11 11.5
Elongation at break, %, approx…………………………… 385 445
Modulus at 100% elongatioin, MPa, approx …………… 2.2 1.9
Tear strength, kN/m, approx………………………………… 21 23
Compression set (22h/177℃/25%), %, approx…………… 35 21
Rebound resilience, %, approx………………………………… 53 50
2. Heat
stability
2.1 Properties after ageing 7 days at 177°C
Shore A hardness, approx…………………………………… 65 65
Tensile strength, MPa, approx………………………………… 10.7 11
Elongation at break, %, approx………………………………… 350 380
Modulus at 100% elongation, MPa, approx………………… 2.5 2.3
Tear strength, kN/m, approx…………………………………… 19 19
Rebound resilience, %, approx………………………………… 55 52
2.2 Properties after ageing 7 days at 200°C
Shore A hardness, approx…………………………………… 65 70
Tensile strength, MPa, approx………………………………… 9.6 8.5
Elongation at break, %, approx………………………………… 305 240
Modulus at 100% elongation, MPa, approx…………………… 2.9 3.4
Tear strength, kN/m, approx…………………………………… 14 13
Rebound resilience, %, approx………………………………… 55 54
2.3 Properties after ageing 10 days at 200°C
Shore A hardness, approx…………………………………… 68 71
Tensile strength, MPa, approx………………………………… 9.2 7.8
Elongation at break, %, approx………………………………… 240 210
Modulus at 100% elongation, MPa, approx…………………… 3.6 3.7
Tear strength, kN/m, approx…………………………………… 10 10
Rebound resilience, %, approx………………………………… 57 57
3. Electrical properties
Dielectric strength (on 1 mm thick slabs), kV/mm, approx……… 29 32
Dielectric strength (on 2 mm thick slabs), kV/mm, approx……… 21 21
Dielectric constant at 1 MHz, approx………………………………… 2.5 3.1
Dielectric factor at 1 MHz, approx…………………………… 3.4×10-3 3.4×10-3
Volume resistivity, Ohm.cm, approx………………………… 2.6×1015 3.2×1015
Packaging: IOTA HCR 160U is delivered in 20 kg carton boxes.
Storage and shelf life: IOTA HCR 160U may be stored in its original unopened packaging at a temperature below 40℃ for up to 18 months from the date of manufacture marked clearly on the packaging.
Past this date, IOTA no longer guarantees that the product meets the sales specifications.
Address: | Sunmoon Industry Park, 985 Xingzhong Road, High-Tech Zone, Bengbu China |
Post Code: |
233000 |
Contact: | Allen |
Telephone: | 0086-552-3827158 |
Fax: |
|
Mobile: | 0086-15605528186 |
Email: | allenwang@siliconeoil.net |
QQ: |
|