HEAT CURED SILICONE RUBBER IOTA HCR 370 U
Description:IOTA HCR 370 U is a very transparent silicone heat-curing elastomer which vulcanizes after the addition of a vulcanizing agent selected in accordance with the transformation process.
Applications:Molding and extrusion of transparent parts with high mechanical properties.
Special properties:
Only slight freshening required
Short post cure
High transparency
High mechanical properties
Characteristics:
Type(in accordance with GB/T 5576/1997) ………………………………………… VMQ
Density at 25℃, g/cm3, approx………………………………………………………… 1.18
Aspect…………………………………………………………………Colorless, transparent
Properties after working:
(1) After addition of 1.25% 2,4-dichloro-benzoyl peroxide (at 50%), and vulcanization for 8min at 115℃
(2) After addition of 1.0% 2,5-dimethyl-2,5-di(tert-butylperoxy)hexane at 45%, and vulcanization for 10 minutes at 170℃
1. Mechanical properties
1.1 Properties without post-cure (1) (2)
Shore A hardness, approx………………………………. 65 68
Tensile strength, MPa, approx…………………………… 9.1 8.9
Elongation at break, %, approx………………………… 520 540
Modulus at 100% elongatioin, MPa, approx ………… 2.4 2.3
Tear strength, kN/m, approx……………………………… 44 43
Rebound resilience, %, approx…………………………… 35 36
Linear shrinkage, %, approx. ……………………………… 2.7 3.7
1.2 Properties after post-cure for 4 hours at 200℃
Shore A hardness, approx………………………………. 70 74
Tensile strength, MPa, approx…………………………… 9.3 9.6
Elongation at break, %, approx……………………… 440 450
Modulus at 100% elongatioin, MPa, approx ……… 2.9 3.5
Tear strength, kN/m, approx…………………………… 40 41
Compression set (22h/177℃/25%), %, approx……… 52 38
Rebound resilience, %, approx………………………… 36 38
Linear shrinkage, %, approx. ……………………………… 3.3 4.3
2. Heat stability
Properties after ageing 7 days at 177°C
Shore A hardness, approx……………………………… 75 80
Tensile strength, MPa, approx…………………………… 8.1 7.6
Elongation at break, %, approx………………………… 240 200
Packaging: IOTA HCR 370 U is delivered in 20 kg carton boxes.
Storage and shelf life: IOTA HCR 370 U may be stored in its original unopened packaging at a temperature below 40℃ for up to 18 months from the date of manufacture marked clearly on the packaging.
Past this date, IOTA no longer guarantees that the product meets the sales specifications.