Methylphenyl silicone resin IOTA 6152
Methyl phenyl silicone resin IOTA 6152
Features:
It has excellent electrical insulation performance, high and low temperature
resistance, water and moisture resistance, weather resistance, ozone resistance
and chemical stability, and good flexibility.
Appearance |
milk-white light alowed, no mechanical impurities, light yellow to reddish brown transparent liquid. |
Solid content % |
≥55 |
Viscosity s/T-4,25℃ |
25-75 |
Drying time |
≤2h/200℃ |
Heat tolerance |
>200h/200℃ |
Loss on heat 3h/250℃,% |
≤3 |
Features and Main application |
glass cloth used for the electric insulation of engines. |
Application:
It is widely used as the base resin for high temperature resistant coatings and
special coatings, as well as general high and low temperature resistant
insulating impregnating paints, covering paints (varnishes, paints, enamels,
etc.), and H-class electrical insulating materials.
Usage :
1. According to the
construction process, can be specified by adding diluent conditioning solid
content and Viscosity. to control the thickness of the coating, usually
adjusted for spraying viscosity 15-25 seconds; diluent should not contain
water, sulfur and other impurities. The coating adhesive force will be
affected, so was stem and other properties.
2. When in use, it should be avoided with acid and alkali, organic acids and
amines contact, otherwise it will accelerate ageing, affect the performance of
the product.
3. At work, according to the resin NO and the use of different requirements and
then confirm dying condition, for high temperature dying type, it should be
solvent dying to volatile at a lower temperature (120 or 160 ° C). Finally
curing at 220 ℃.
4. Resin has good compatibility with heat resistant pigments (aluminum, glass
bead, low-density ceramic powder. Black chromium oxide and iron oxide powder,
etc.), the coating should be dipping, spraying, brush and other construction
methods, curing the coating can be used in 250-400 ℃. Some may be resistant
500-600 ° C, even higher temperatures.
5. Application examples of reference:
(1) fire-resistant insulation coating formula :
silicone resin |
Higher chlorinated polyethylene |
epoxy resinF-644 |
Polyamide resin |
Padding |
Flux |
Titanate |
40-60Copies |
5-15Copies |
10-20Copies |
4-12Copies |
45-85Copies |
5-15Copies |
1-2Copies |
All material will be
transferred into a paste, and then grinding with sand mill 20 ~ 30min after the
addition of solvent dispersion, and then filter.
(2) fire-resistant aluminum section formula :
60% Methylphenyl silicone resin |
65%Aluminum Paste |
xylene |
Dispersant |
76Copies |
26Copies |
46Copies |
2Copies |
Put aluminum paste into a
container, add a small amount of resin, stir slowly, add disperser and residual
resin, added xylene to construction of viscosity after fully stirred, with 120
mesh silk filter then finish.
Safety Note :
1. Resin contains flammable, explosive and toxic solvents, In the process of
use and processing, should pay attention to the site operation ventilation, to
prevent fire, strengthening the protection of workers.
2. During transportation and storage, prevent sunlight, fire and heat protection,
pay attention to warehouse ventilation.
3. Packed with galvanized iron sheet barrel, storage period is generally 6
months, if pass storage period, please test it strictly and then use. Avoid
heat, otherwise it will reduce the storage stability.
Address: | Sunmoon Industry Park, 985 Xingzhong Road, High-Tech Zone, Bengbu China |
Post Code: |
233000 |
Contact: | Allen |
Telephone: | 0086-552-3827158 |
Fax: |
|
Mobile: | 0086-15605528186 |
Email: | allenwang@siliconeoil.net |
QQ: |
|