Unsaturated resin release agent IOTA 55-NC
Introductions:

IOTA 55-NC is another type of IOTA 44-NC with fast evaporation and low odor. The main ingredients of IOTA 55-NC is similar to IOTA 44-NC. Eexcept that there is a litter solvent changed. IOTA 55-NC is your best choice under the application that requires the release agent not to transfer to the surface of the article. This semi-permanent release agent that has non-transfer and the surface of Molds forms a coating layer by a chemical bond, which is stable under most molding temperature conditions. IOTA 55-NC can be used for these materials：Epoxy resins, unsaturated polyester resins, thermoplastics, adhesives and plastics rotational molding.

Features：

Quick-drying ＜1 minute

No transfer

No fouling

High thermal stability

Low/no odor

Higher utilization of Mold 

Physical and Chemical Properties：

Appearance ：Transparent liquid

Oder ： Hydrocarbons

Solvent ： Aliphatic hydrocarbon

proportion ： 0.720±0.010

Shelf Life ： Save one year from the date of production

Precautions ： Sensitive to moisture, cover the lid  when iit is 
not in use

Cured thermal stability ：400℃（750°F）

Operating temperature ：20℃-60℃ (68°F-140°F) 

Mold preparation：

To make sure the best use results of IOTA 55-NC, ensure that molds surface is clean, dry and free of any release agent residues and contaminants. You can use fine industrial abrasives to handle thick resin fouling.  

New moldings：

We recommend that the new mold be fully cured, in order to ensure good bonding effect mold release agents and mold surface. For fiberglass molds prior,ensure that it is fully cured according to the mold material supplier's recommendations.

note：For porous or repaired Molds, IOTA Sealer should be used ---refer to its Technical Information. If necessary, ask technical representative for support. 

Instructions：* Refer to Material Safety Data Sheet Before using *

IOTA 55-NC can be applied to the surface of the mold by spraying, brushing or Wiping by towels that are and have no scrap under the conditions of room temperature to 60 ℃. Ensure dry air source or use airless system at the progress of spraying. Ensure the construction is at a well-ventilated place.

1. Forming a thin and wet coating on the surface of molds. Avoid working at area where is wiping or sprayed just now, and wait until the Solvent Completely volatilized. We recommend spraying nozzle are away from the mold surface for 20-30cm (8-10 inches). It is better to spray from side to side.

2. Coated 2-3 Road, the interval between each channel  needs 5 minutes to evaporate the solvent.

3. The last coating should be cured for 30 minutes at room temperature or cured at 100-150 ° C for 5 minutes.

4. When the mold surface adapted to IOTA, it will be the best result. If fill the mold after several Release time , there will be better.

5. When difficulties arise at the progress of release, you can select to cover the entire Molds again, or only fix the difficult places. once in Release to fix difficult places.

Remark：The progress of filling the mold will be better before the unspoiled, this can increase the efficiency and reduce Release resin fouling possible.

note：When it is used for closing mold processes (such as rotational molding), Make sure the complete evaporation of the solvent and to ensure that all of the solvent vapor discharge cavity before clamping. It is available to assist exhaust by oil-free compressed air.

Flammability and storage